UL Certification
Polystar-60G(xx), PA6, HB, 1.5mm
|
60G (xx) Polyamide 6 (PA6) – furnished as pellets |
|
Min Thickness |
Flame |
|
|
RTI |
RTI |
RTI |
|
Color |
(mm) |
Class |
HWI |
HAI |
Elec |
Imp |
Str |
|
ALL |
1.5 |
HB |
4 |
0 |
65 |
65 |
65 |
|
3.0 |
HB |
4 |
0 |
65 |
65 |
65 |
|
Comparative Tracking Index (CTI): 1 |
Dimensional Stability (%): - |
|
|
High-Voltage Arc Tracking Rate (HVTR): 1 |
High Volt, Low Current Arc Resis (D495): 5 |
|
|
Dielectric Strength (kV/mm): - |
Volume Resistivity (10x ohm-cm): - |
|
(xx) - Represents a one or two digit number denoting glass content from 0 to 50. |
Polystar-66F2, PA66, V-0, 0.40-0.44mm
|
66F2 Polyamide 66 (PA66) – furnished as pellets |
|
Min Thickness |
Flame |
|
|
RTI |
RTI |
RTI |
|
Color |
(mm) |
Class |
HWI |
HAI |
Elec |
Imp |
Str |
|
ALL |
0.40 – 0.44 |
V-0 |
4 |
1 |
65 |
65 |
65 |
|
Comparative Tracking Index (CTI): 0 |
Dimensional Stability (%): - |
|
|
High-Voltage Arc Tracking Rate (HVTR): 3 |
High Volt, Low Current Arc Resis (D495): 5 |
|
|
Dielectric Strength (kV/mm): - |
Volume Resistivity (10x ohm-cm): - |
Polystar-66G(xx)H, PA66, HB, 1.5mm
|
66G (xx) H Polyamide 66 (PA66) – furnished as pellets |
|
Min Thickness |
Flame |
|
|
RTI |
RTI |
RTI |
|
Color |
(mm) |
Class |
HWI |
HAI |
Elec |
Imp |
Str |
|
ALL |
1.5 |
HB |
4 |
0 |
65 |
65 |
65 |
|
3.0 |
HB |
4 |
0 |
65 |
65 |
65 |
|
Comparative Tracking Index (CTI): 1 |
Dimensional Stability (%): - |
|
|
High-Voltage Arc Tracking Rate (HVTR): 3 |
High Volt, Low Current Arc Resis (D495): 5 |
|
|
Dielectric Strength (kV/mm): - |
Volume Resistivity (10x ohm-cm): - |
|
(xx) - Represents a one or two digit number denoting glass content from 0 to 50. |
Polystar-66G(xx)F1, PA66, V-0, 1.5mm
|
66G (xx) F1 Polyamide 66 (PA66) – furnished as pellets |
|
Min Thickness |
Flame |
|
|
RTI |
RTI |
RTI |
|
Color |
(mm) |
Class |
HWI |
HAI |
Elec |
Imp |
Str |
|
ALL |
1.5 |
V-0 |
3 |
0 |
65 |
65 |
65 |
|
3.0 |
V-0 |
0 |
0 |
65 |
65 |
65 |
|
Comparative Tracking Index (CTI): 2 |
Dimensional Stability (%): - |
|
|
High-Voltage Arc Tracking Rate (HVTR): 3 |
High Volt, Low Current Arc Resis (D495): 5 |
|
|
Dielectric Strength (kV/mm): - |
Volume Resistivity (10x ohm-cm): - |
|
(xx) - Represents a one or two digit number denoting glass content from 0 to 50. |
Polystar-70G(yy)F1, PC, V-0, 1.5mm
|
70G (yy) F1 Polycarbonate (PC) – furnished as pellets |
|
Min Thickness |
Flame |
|
|
RTI |
RTI |
RTI |
|
Color |
(mm) |
Class |
HWI |
HAI |
Elec |
Imp |
Str |
|
ALL |
1.5 |
V-0 |
2 |
3 |
80 |
80 |
80 |
|
3.0 |
V-0 |
2 |
3 |
80 |
80 |
80 |
|
Comparative Tracking Index (CTI): 4 |
Dimensional Stability (%): - |
|
|
High-Voltage Arc Tracking Rate (HVTR): 4 |
High Volt, Low Current Arc Resis (D495): 6 |
|
|
Dielectric Strength (kV/mm): - |
Volume Resistivity (10x ohm-cm): - |
|
(xx) - Represents a one or two digit number denoting glass content from 0 to 40. |
Polystar-85G(xx)F1, PBT, V-0, 1.5mm
|
85G (xx) F1 Polybutylene Terephthalate (PBT) – furnished as pellets |
|
Min Thickness |
Flame |
|
|
RTI |
RTI |
RTI |
|
Color |
(mm) |
Class |
HWI |
HAI |
Elec |
Imp |
Str |
|
ALL |
1.5 |
V-0 |
3 |
2 |
75 |
75 |
75 |
|
3.0 |
V-0 |
3 |
2 |
75 |
75 |
75 |
|
Comparative Tracking Index (CTI): 4 |
Dimensional Stability (%): - |
|
|
High-Voltage Arc Tracking Rate (HVTR): 4 |
High Volt, Low Current Arc Resis (D495): 5 |
|
|
Dielectric Strength (kV/mm): - |
Volume Resistivity (10x ohm-cm): - |
|
(xx) - Represents a one or two digit number denoting glass content from 0 to 50. |